C90900 Bronze vs. CC484K Bronze
Both C90900 bronze and CC484K bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have a very high 99% of their average alloy composition in common.
For each property being compared, the top bar is C90900 bronze and the bottom bar is CC484K bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 90 | |
| 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 15 | |
| 11 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 330 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 170 |
| Melting Completion (Liquidus), °C | 980 | |
| 1000 |
| Melting Onset (Solidus), °C | 820 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 360 | |
| 370 |
| Thermal Conductivity, W/m-K | 65 | |
| 70 |
| Thermal Expansion, µm/m-K | 18 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 9.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 9.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 37 |
| Density, g/cm3 | 8.7 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 3.9 | |
| 3.9 |
| Embodied Energy, MJ/kg | 64 | |
| 64 |
| Embodied Water, L/kg | 410 | |
| 400 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 35 | |
| 32 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 89 | |
| 180 |
| Stiffness to Weight: Axial, points | 6.8 | |
| 6.9 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 8.8 | |
| 10 |
| Strength to Weight: Bending, points | 11 | |
| 12 |
| Thermal Diffusivity, mm2/s | 21 | |
| 22 |
| Thermal Shock Resistance, points | 10 | |
| 12 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.010 |
| Antimony (Sb), % | 0 to 0.2 | |
| 0 to 0.1 |
| Copper (Cu), % | 86 to 89 | |
| 84.5 to 87.5 |
| Iron (Fe), % | 0 to 0.15 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 to 0.25 | |
| 0 to 0.3 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 to 0.5 | |
| 1.5 to 2.5 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0.050 to 0.4 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.050 |
| Tin (Sn), % | 12 to 14 | |
| 11 to 13 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.4 |
| Residuals, % | 0 to 0.6 | |
| 0 |