C91000 bronze belongs to the copper alloys classification, while AWS BAg-19 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is C91000 bronze and the bottom bar is AWS BAg-19.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
74
Poisson's Ratio 0.34
0.37
Shear Modulus, GPa 39
27
Tensile Strength: Ultimate (UTS), MPa 230
140

Thermal Properties

Latent Heat of Fusion, J/g 180
120
Melting Completion (Liquidus), °C 960
890
Melting Onset (Solidus), °C 820
760
Specific Heat Capacity, J/kg-K 360
250
Thermal Expansion, µm/m-K 18
20

Otherwise Unclassified Properties

Density, g/cm3 8.6
10

Common Calculations

Stiffness to Weight: Axial, points 6.8
4.0
Stiffness to Weight: Bending, points 18
14
Strength to Weight: Axial, points 7.5
3.8
Strength to Weight: Bending, points 9.7
5.8
Thermal Shock Resistance, points 8.8
6.9

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.2
0
Copper (Cu), % 84 to 86
6.6 to 7.9
Iron (Fe), % 0 to 0.1
0
Lead (Pb), % 0 to 0.2
0
Lithium (Li), % 0
0.15 to 0.3
Nickel (Ni), % 0 to 0.8
0
Phosphorus (P), % 0 to 1.5
0
Silicon (Si), % 0 to 0.0050
0
Silver (Ag), % 0
92 to 93
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 14 to 16
0
Zinc (Zn), % 0 to 1.5
0
Residuals, % 0
0 to 0.15