C91300 Bell Metal vs. EN 2.4668 Nickel
C91300 bell metal belongs to the copper alloys classification, while EN 2.4668 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C91300 bell metal and the bottom bar is EN 2.4668 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 0.5 | |
| 14 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 38 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 240 | |
| 1390 |
| Tensile Strength: Yield (Proof), MPa | 210 | |
| 1160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 150 | |
| 980 |
| Melting Completion (Liquidus), °C | 890 | |
| 1460 |
| Melting Onset (Solidus), °C | 820 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 360 | |
| 450 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 1.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.4 | |
| 1.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 39 | |
| 75 |
| Density, g/cm3 | 8.6 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 4.5 | |
| 13 |
| Embodied Energy, MJ/kg | 74 | |
| 190 |
| Embodied Water, L/kg | 460 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 1.1 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 | |
| 3490 |
| Stiffness to Weight: Axial, points | 6.6 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 23 |
| Strength to Weight: Axial, points | 7.8 | |
| 46 |
| Strength to Weight: Bending, points | 10 | |
| 33 |
| Thermal Shock Resistance, points | 9.3 | |
| 40 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0.3 to 0.7 |
| Antimony (Sb), % | 0 to 0.2 | |
| 0 |
| Boron (B), % | 0 | |
| 0.0020 to 0.0060 |
| Carbon (C), % | 0 | |
| 0.020 to 0.080 |
| Chromium (Cr), % | 0 | |
| 17 to 21 |
| Cobalt (Co), % | 0 | |
| 0 to 1.0 |
| Copper (Cu), % | 79 to 82 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 0.25 | |
| 11.2 to 24.6 |
| Lead (Pb), % | 0 to 0.25 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.35 |
| Molybdenum (Mo), % | 0 | |
| 2.8 to 3.3 |
| Nickel (Ni), % | 0 to 0.5 | |
| 50 to 55 |
| Niobium (Nb), % | 0 | |
| 4.7 to 5.5 |
| Phosphorus (P), % | 0 to 1.5 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.35 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.015 |
| Tin (Sn), % | 18 to 20 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0.6 to 1.2 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 |
| Residuals, % | 0 to 0.6 | |
| 0 |