C91300 Bell Metal vs. Grade N12MV Nickel

C91300 bell metal belongs to the copper alloys classification, while grade N12MV nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C91300 bell metal and the bottom bar is grade N12MV nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
220
Elongation at Break, % 0.5
6.8
Poisson's Ratio 0.34
0.31
Shear Modulus, GPa 38
84
Tensile Strength: Ultimate (UTS), MPa 240
600
Tensile Strength: Yield (Proof), MPa 210
310

Thermal Properties

Latent Heat of Fusion, J/g 180
320
Maximum Temperature: Mechanical, °C 150
900
Melting Completion (Liquidus), °C 890
1620
Melting Onset (Solidus), °C 820
1570
Specific Heat Capacity, J/kg-K 360
390
Thermal Expansion, µm/m-K 18
10

Otherwise Unclassified Properties

Base Metal Price, % relative 39
75
Density, g/cm3 8.6
9.2
Embodied Carbon, kg CO2/kg material 4.5
16
Embodied Energy, MJ/kg 74
200
Embodied Water, L/kg 460
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 1.1
34
Resilience: Unit (Modulus of Resilience), kJ/m3 210
220
Stiffness to Weight: Axial, points 6.6
13
Stiffness to Weight: Bending, points 18
22
Strength to Weight: Axial, points 7.8
18
Strength to Weight: Bending, points 10
17
Thermal Shock Resistance, points 9.3
19

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.2
0
Carbon (C), % 0
0 to 0.12
Chromium (Cr), % 0
0 to 1.0
Copper (Cu), % 79 to 82
0
Iron (Fe), % 0 to 0.25
4.0 to 6.0
Lead (Pb), % 0 to 0.25
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
26 to 30
Nickel (Ni), % 0 to 0.5
60.2 to 69.8
Phosphorus (P), % 0 to 1.5
0 to 0.040
Silicon (Si), % 0 to 0.0050
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.030
Tin (Sn), % 18 to 20
0
Vanadium (V), % 0
0.2 to 0.6
Zinc (Zn), % 0 to 0.25
0
Residuals, % 0 to 0.6
0