C92300 Bronze vs. N08028 Stainless Steel
C92300 bronze belongs to the copper alloys classification, while N08028 stainless steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C92300 bronze and the bottom bar is N08028 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 19 | |
| 45 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 40 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 300 | |
| 570 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1000 | |
| 1420 |
| Melting Onset (Solidus), °C | 850 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 370 | |
| 470 |
| Thermal Conductivity, W/m-K | 75 | |
| 12 |
| Thermal Expansion, µm/m-K | 18 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 37 |
| Density, g/cm3 | 8.7 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 6.4 |
| Embodied Energy, MJ/kg | 56 | |
| 89 |
| Embodied Water, L/kg | 370 | |
| 240 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 47 | |
| 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 86 | |
| 140 |
| Stiffness to Weight: Axial, points | 6.9 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 9.5 | |
| 19 |
| Strength to Weight: Bending, points | 11 | |
| 19 |
| Thermal Diffusivity, mm2/s | 23 | |
| 3.2 |
| Thermal Shock Resistance, points | 11 | |
| 12 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 0 to 0.25 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 26 to 28 |
| Copper (Cu), % | 85 to 89 | |
| 0.6 to 1.4 |
| Iron (Fe), % | 0 to 0.25 | |
| 29 to 40.4 |
| Lead (Pb), % | 0.3 to 1.0 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 2.5 |
| Molybdenum (Mo), % | 0 | |
| 3.0 to 4.0 |
| Nickel (Ni), % | 0 to 1.0 | |
| 30 to 34 |
| Phosphorus (P), % | 0 to 1.5 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.030 |
| Tin (Sn), % | 7.5 to 9.0 | |
| 0 |
| Zinc (Zn), % | 2.5 to 5.0 | |
| 0 |
| Residuals, % | 0 to 0.7 | |
| 0 |