C92600 Bronze vs. S32550 Stainless Steel

C92600 bronze belongs to the copper alloys classification, while S32550 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C92600 bronze and the bottom bar is S32550 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 70
260
Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 30
21
Poisson's Ratio 0.34
0.27
Shear Modulus, GPa 40
80
Tensile Strength: Ultimate (UTS), MPa 300
860
Tensile Strength: Yield (Proof), MPa 140
620

Thermal Properties

Latent Heat of Fusion, J/g 190
300
Maximum Temperature: Mechanical, °C 170
1100
Melting Completion (Liquidus), °C 980
1440
Melting Onset (Solidus), °C 840
1390
Specific Heat Capacity, J/kg-K 370
480
Thermal Conductivity, W/m-K 67
16
Thermal Expansion, µm/m-K 18
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 9.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 34
20
Density, g/cm3 8.7
7.8
Embodied Carbon, kg CO2/kg material 3.6
3.8
Embodied Energy, MJ/kg 58
53
Embodied Water, L/kg 390
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 74
160
Resilience: Unit (Modulus of Resilience), kJ/m3 88
940
Stiffness to Weight: Axial, points 6.8
14
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 9.6
31
Strength to Weight: Bending, points 11
26
Thermal Diffusivity, mm2/s 21
4.4
Thermal Shock Resistance, points 11
23

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.25
0
Carbon (C), % 0
0 to 0.040
Chromium (Cr), % 0
24 to 27
Copper (Cu), % 86 to 88.5
1.5 to 2.5
Iron (Fe), % 0 to 0.2
57.2 to 67
Lead (Pb), % 0.8 to 1.5
0
Manganese (Mn), % 0
0 to 1.5
Molybdenum (Mo), % 0
2.9 to 3.9
Nickel (Ni), % 0 to 0.7
4.5 to 6.5
Nitrogen (N), % 0
0.1 to 0.25
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.0050
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.030
Tin (Sn), % 9.3 to 10.5
0
Zinc (Zn), % 1.3 to 2.5
0
Residuals, % 0 to 0.7
0