C92700 Bronze vs. Solder Alloy 191

C92700 bronze belongs to the copper alloys classification, while solder alloy 191 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C92700 bronze and the bottom bar is solder alloy 191.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
19
Elongation at Break, % 9.1
32
Poisson's Ratio 0.34
0.43
Shear Modulus, GPa 40
6.5
Tensile Strength: Ultimate (UTS), MPa 290
29

Thermal Properties

Latent Heat of Fusion, J/g 190
27
Melting Completion (Liquidus), °C 980
300
Melting Onset (Solidus), °C 840
300
Specific Heat Capacity, J/kg-K 370
130
Thermal Conductivity, W/m-K 47
24
Thermal Expansion, µm/m-K 18
29

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
8.8
Electrical Conductivity: Equal Weight (Specific), % IACS 11
7.2

Otherwise Unclassified Properties

Density, g/cm3 8.7
11
Embodied Carbon, kg CO2/kg material 3.6
5.8
Embodied Energy, MJ/kg 58
95

Common Calculations

Stiffness to Weight: Axial, points 6.8
0.93
Stiffness to Weight: Bending, points 18
8.0
Strength to Weight: Axial, points 9.1
0.72
Strength to Weight: Bending, points 11
1.9
Thermal Diffusivity, mm2/s 15
16
Thermal Shock Resistance, points 11
3.9

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0 to 0.0010
Antimony (Sb), % 0 to 0.25
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 86 to 89
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.2
0 to 0.020
Lead (Pb), % 1.0 to 2.5
92.4 to 94
Nickel (Ni), % 0 to 1.0
0 to 0.010
Phosphorus (P), % 0 to 1.5
0
Silicon (Si), % 0 to 0.0050
0
Silver (Ag), % 0
1.2 to 1.8
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 9.0 to 11
4.8 to 5.2
Zinc (Zn), % 0 to 0.7
0 to 0.0010
Residuals, % 0 to 0.7
0