C93700 Bronze vs. C67600 Bronze
Both C93700 bronze and C67600 bronze are copper alloys. They have 61% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C93700 bronze and the bottom bar is C67600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 99 | |
| 100 |
| Elongation at Break, % | 20 | |
| 13 to 33 |
| Poisson's Ratio | 0.35 | |
| 0.31 |
| Shear Modulus, GPa | 37 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 240 | |
| 430 to 570 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 170 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 120 |
| Melting Completion (Liquidus), °C | 930 | |
| 890 |
| Melting Onset (Solidus), °C | 760 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 350 | |
| 380 |
| Thermal Conductivity, W/m-K | 47 | |
| 110 |
| Thermal Expansion, µm/m-K | 19 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 24 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 23 |
| Density, g/cm3 | 8.9 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 3.5 | |
| 2.8 |
| Embodied Energy, MJ/kg | 57 | |
| 47 |
| Embodied Water, L/kg | 390 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 40 | |
| 63 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 79 | |
| 140 to 680 |
| Stiffness to Weight: Axial, points | 6.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 17 | |
| 20 |
| Strength to Weight: Axial, points | 7.5 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 9.6 | |
| 16 to 19 |
| Thermal Diffusivity, mm2/s | 15 | |
| 35 |
| Thermal Shock Resistance, points | 9.4 | |
| 14 to 19 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 78 to 82 | |
| 57 to 60 |
| Iron (Fe), % | 0 to 0.15 | |
| 0.4 to 1.3 |
| Lead (Pb), % | 8.0 to 11 | |
| 0.5 to 1.0 |
| Manganese (Mn), % | 0 | |
| 0.050 to 0.5 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 1.5 | |
| 0 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Sulfur (S), % | 0 to 0.080 | |
| 0 |
| Tin (Sn), % | 9.0 to 11 | |
| 0.5 to 1.5 |
| Zinc (Zn), % | 0 to 0.8 | |
| 35.2 to 41.6 |
| Residuals, % | 0 | |
| 0 to 0.5 |