C93900 Bronze vs. C94300 Bronze
Both C93900 bronze and C94300 bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have a moderately high 93% of their average alloy composition in common.
For each property being compared, the top bar is C93900 bronze and the bottom bar is C94300 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 95 | |
| 87 |
| Elongation at Break, % | 5.6 | |
| 9.7 |
| Poisson's Ratio | 0.36 | |
| 0.36 |
| Shear Modulus, GPa | 35 | |
| 32 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 180 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 150 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 110 |
| Melting Completion (Liquidus), °C | 940 | |
| 820 |
| Melting Onset (Solidus), °C | 850 | |
| 760 |
| Specific Heat Capacity, J/kg-K | 340 | |
| 320 |
| Thermal Conductivity, W/m-K | 52 | |
| 63 |
| Thermal Expansion, µm/m-K | 19 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 28 |
| Density, g/cm3 | 9.1 | |
| 9.3 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 2.9 |
| Embodied Energy, MJ/kg | 49 | |
| 47 |
| Embodied Water, L/kg | 360 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.5 | |
| 15 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 83 | |
| 77 |
| Stiffness to Weight: Axial, points | 5.8 | |
| 5.2 |
| Stiffness to Weight: Bending, points | 17 | |
| 16 |
| Strength to Weight: Axial, points | 5.9 | |
| 5.2 |
| Strength to Weight: Bending, points | 8.1 | |
| 7.4 |
| Thermal Diffusivity, mm2/s | 17 | |
| 21 |
| Thermal Shock Resistance, points | 7.5 | |
| 7.1 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 to 0.8 |
| Copper (Cu), % | 76.5 to 79.5 | |
| 67 to 72 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.15 |
| Lead (Pb), % | 14 to 18 | |
| 23 to 27 |
| Nickel (Ni), % | 0 to 0.8 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 1.5 | |
| 0 to 1.5 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.080 | |
| 0 to 0.080 |
| Tin (Sn), % | 5.0 to 7.0 | |
| 4.5 to 6.0 |
| Zinc (Zn), % | 0 to 1.5 | |
| 0 to 0.8 |
| Residuals, % | 0 | |
| 0 to 1.0 |