C94700 Bronze vs. C91700 Bronze
Both C94700 bronze and C91700 bronze are copper alloys. They have a moderately high 93% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C94700 bronze and the bottom bar is C91700 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 7.9 to 32 | |
| 13 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 590 | |
| 330 |
| Tensile Strength: Yield (Proof), MPa | 160 to 400 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 170 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1020 |
| Melting Onset (Solidus), °C | 900 | |
| 850 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 370 |
| Thermal Conductivity, W/m-K | 54 | |
| 71 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 36 |
| Density, g/cm3 | 8.8 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 3.5 | |
| 3.9 |
| Embodied Energy, MJ/kg | 56 | |
| 63 |
| Embodied Water, L/kg | 350 | |
| 400 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 41 to 89 | |
| 35 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 700 | |
| 140 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 6.9 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 11 to 19 | |
| 11 |
| Strength to Weight: Bending, points | 13 to 18 | |
| 12 |
| Thermal Diffusivity, mm2/s | 16 | |
| 22 |
| Thermal Shock Resistance, points | 12 to 21 | |
| 12 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 to 0.15 | |
| 0 to 0.2 |
| Copper (Cu), % | 85 to 90 | |
| 84.2 to 87.5 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 to 0.25 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 |
| Nickel (Ni), % | 4.5 to 6.0 | |
| 1.2 to 2.0 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0 to 0.3 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.050 |
| Tin (Sn), % | 4.5 to 6.0 | |
| 11.3 to 12.5 |
| Zinc (Zn), % | 1.0 to 2.5 | |
| 0 to 0.25 |
| Residuals, % | 0 to 1.3 | |
| 0 |