C95200 Bronze vs. Grade 704C Zirconium

C95200 bronze belongs to the copper alloys classification, while grade 704C zirconium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is C95200 bronze and the bottom bar is grade 704C zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
210
Elastic (Young's, Tensile) Modulus, GPa 110
97
Elongation at Break, % 29
11
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 42
36
Tensile Strength: Ultimate (UTS), MPa 520
470
Tensile Strength: Yield (Proof), MPa 190
310

Thermal Properties

Latent Heat of Fusion, J/g 230
240
Specific Heat Capacity, J/kg-K 430
270
Thermal Conductivity, W/m-K 50
21
Thermal Expansion, µm/m-K 18
5.9

Otherwise Unclassified Properties

Density, g/cm3 8.3
6.7
Embodied Water, L/kg 380
460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
48
Resilience: Unit (Modulus of Resilience), kJ/m3 170
490
Stiffness to Weight: Axial, points 7.6
8.1
Stiffness to Weight: Bending, points 19
23
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 14
12
Thermal Shock Resistance, points 19
58

Alloy Composition

Aluminum (Al), % 8.5 to 9.5
0
Carbon (C), % 0
0 to 0.1
Copper (Cu), % 86 to 89
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 2.5 to 4.0
0 to 0.3
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.010
Tin (Sn), % 0
1.0 to 2.0
Zirconium (Zr), % 0
92.9 to 99
Residuals, % 0 to 1.0
0