C95410 Bronze vs. N12160 Nickel
C95410 bronze belongs to the copper alloys classification, while N12160 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C95410 bronze and the bottom bar is N12160 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 210 |
| Elongation at Break, % | 9.1 to 13 | |
| 45 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 740 | |
| 710 |
| Tensile Strength: Yield (Proof), MPa | 260 to 380 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 360 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 1060 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1330 |
| Melting Onset (Solidus), °C | 1030 | |
| 1280 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Conductivity, W/m-K | 59 | |
| 11 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 90 |
| Density, g/cm3 | 8.2 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 8.5 |
| Embodied Energy, MJ/kg | 54 | |
| 120 |
| Embodied Water, L/kg | 390 | |
| 400 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 57 to 64 | |
| 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 630 | |
| 180 |
| Stiffness to Weight: Axial, points | 7.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 21 to 25 | |
| 24 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 22 |
| Thermal Diffusivity, mm2/s | 16 | |
| 2.8 |
| Thermal Shock Resistance, points | 22 to 26 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 10 to 11.5 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 26 to 30 |
| Cobalt (Co), % | 0 | |
| 27 to 33 |
| Copper (Cu), % | 83 to 85.5 | |
| 0 |
| Iron (Fe), % | 3.0 to 5.0 | |
| 0 to 3.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 1.5 to 2.5 | |
| 25 to 44.4 |
| Niobium (Nb), % | 0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 2.4 to 3.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.2 to 0.8 |
| Tungsten (W), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 to 0.5 | |
| 0 |