C95500 Bronze vs. EN 1.3570 Steel
C95500 bronze belongs to the copper alloys classification, while EN 1.3570 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C95500 bronze and the bottom bar is EN 1.3570 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 210 | |
| 150 to 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 44 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 850 | |
| 490 to 1440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 410 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1460 |
| Melting Onset (Solidus), °C | 1040 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 42 | |
| 46 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 2.3 |
| Density, g/cm3 | 8.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.5 | |
| 1.5 |
| Embodied Energy, MJ/kg | 57 | |
| 19 |
| Embodied Water, L/kg | 390 | |
| 50 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.0 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 24 to 29 | |
| 17 to 51 |
| Strength to Weight: Bending, points | 21 to 24 | |
| 18 to 36 |
| Thermal Diffusivity, mm2/s | 11 | |
| 13 |
| Thermal Shock Resistance, points | 24 to 29 | |
| 14 to 42 |
Alloy Composition
| Aluminum (Al), % | 10 to 11.5 | |
| 0 to 0.050 |
| Carbon (C), % | 0 | |
| 0.17 to 0.23 |
| Chromium (Cr), % | 0 | |
| 0.4 to 0.75 |
| Copper (Cu), % | 78 to 84 | |
| 0 to 0.3 |
| Iron (Fe), % | 3.0 to 5.0 | |
| 97.1 to 98.9 |
| Manganese (Mn), % | 0 to 3.5 | |
| 0.65 to 1.1 |
| Molybdenum (Mo), % | 0 | |
| 0.1 to 0.2 |
| Nickel (Ni), % | 3.0 to 5.5 | |
| 0 |
| Oxygen (O), % | 0 | |
| 0 to 0.0020 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Residuals, % | 0 to 0.5 | |
| 0 |