C95600 Bronze vs. AWS BNi-9

C95600 bronze belongs to the copper alloys classification, while AWS BNi-9 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is C95600 bronze and the bottom bar is AWS BNi-9.

UNS C95600 Silicon-Aluminum Bronze AWS BNi-9 (N99612) Filler Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		110
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.34
Poisson's Ratio		0.3

Shear Modulus, GPa		42
Shear Modulus, GPa		72

Tensile Strength: Ultimate (UTS), MPa		500
Tensile Strength: Ultimate (UTS), MPa		580

Thermal Properties

Latent Heat of Fusion, J/g		260
Latent Heat of Fusion, J/g		300

Melting Completion (Liquidus), °C		1000
Melting Completion (Liquidus), °C		1060

Melting Onset (Solidus), °C		980
Melting Onset (Solidus), °C		1060

Specific Heat Capacity, J/kg-K		430
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		28
Base Metal Price, % relative		60

Density, g/cm³		8.3
Density, g/cm³		8.4

Embodied Carbon, kg CO₂/kg material		3.0
Embodied Carbon, kg CO₂/kg material		9.3

Embodied Energy, MJ/kg		50
Embodied Energy, MJ/kg		130

Embodied Water, L/kg		360
Embodied Water, L/kg		260

Common Calculations

Stiffness to Weight: Axial, points		7.5
Stiffness to Weight: Axial, points		12

Stiffness to Weight: Bending, points		19
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		17
Strength to Weight: Axial, points		19

Strength to Weight: Bending, points		17
Strength to Weight: Bending, points		18

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		19

Alloy Composition

Aluminum (Al), %		6.0 to 8.0
Aluminum (Al), %		0 to 0.050

Boron (B), %		0
Boron (B), %		3.3 to 4.0

Carbon (C), %		0
Carbon (C), %		0 to 0.060

Chromium (Cr), %		0
Chromium (Cr), %		13.5 to 16.5

Cobalt (Co), %		0
Cobalt (Co), %		0 to 0.1

Copper (Cu), %		88 to 92.2
Copper (Cu), %		0

Iron (Fe), %		0
Iron (Fe), %		0 to 1.5

Nickel (Ni), %		0 to 0.25
Nickel (Ni), %		77.1 to 83.3

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.020

Selenium (Se), %		0
Selenium (Se), %		0 to 0.0050

Silicon (Si), %		1.8 to 3.2
Silicon (Si), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.020

Titanium (Ti), %		0
Titanium (Ti), %		0 to 0.050

Zirconium (Zr), %		0
Zirconium (Zr), %		0 to 0.050

Residuals, %		0
Residuals, %		0 to 0.5