C95820 Bronze vs. EN 1.5918 Steel
C95820 bronze belongs to the copper alloys classification, while EN 1.5918 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C95820 bronze and the bottom bar is EN 1.5918 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 120 | |
190 |
Poisson's Ratio | 0.34 | |
0.29 |
Shear Modulus, GPa | 44 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 730 | |
530 to 1390 |
Thermal Properties
Latent Heat of Fusion, J/g | 230 | |
250 |
Maximum Temperature: Mechanical, °C | 230 | |
440 |
Melting Completion (Liquidus), °C | 1080 | |
1460 |
Melting Onset (Solidus), °C | 1020 | |
1420 |
Specific Heat Capacity, J/kg-K | 440 | |
470 |
Thermal Conductivity, W/m-K | 38 | |
43 |
Thermal Expansion, µm/m-K | 17 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
7.6 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
8.7 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 29 | |
3.4 |
Density, g/cm3 | 8.3 | |
7.9 |
Embodied Carbon, kg CO2/kg material | 3.5 | |
1.6 |
Embodied Energy, MJ/kg | 56 | |
21 |
Embodied Water, L/kg | 380 | |
56 |
Common Calculations
Stiffness to Weight: Axial, points | 8.0 | |
13 |
Stiffness to Weight: Bending, points | 20 | |
24 |
Strength to Weight: Axial, points | 24 | |
19 to 49 |
Strength to Weight: Bending, points | 22 | |
18 to 35 |
Thermal Diffusivity, mm2/s | 11 | |
12 |
Thermal Shock Resistance, points | 25 | |
15 to 41 |
Alloy Composition
Aluminum (Al), % | 9.0 to 10 | |
0 |
Carbon (C), % | 0 | |
0.14 to 0.2 |
Chromium (Cr), % | 0 | |
1.4 to 1.7 |
Copper (Cu), % | 77.5 to 82.5 | |
0 to 0.25 |
Iron (Fe), % | 4.0 to 5.0 | |
94.9 to 96.6 |
Lead (Pb), % | 0 to 0.020 | |
0 |
Manganese (Mn), % | 0 to 1.5 | |
0.5 to 0.9 |
Nickel (Ni), % | 4.5 to 5.8 | |
1.4 to 1.7 |
Phosphorus (P), % | 0 | |
0 to 0.025 |
Silicon (Si), % | 0 to 0.1 | |
0 to 0.3 |
Sulfur (S), % | 0 | |
0 to 0.025 |
Tin (Sn), % | 0 to 0.020 | |
0 |
Zinc (Zn), % | 0 to 0.2 | |
0 |
Residuals, % | 0 to 0.8 | |
0 |