C96700 Copper vs. Z24311 Zinc
C96700 copper belongs to the copper alloys classification, while Z24311 zinc belongs to the zinc alloys. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C96700 copper and the bottom bar is Z24311 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 87 |
| Elongation at Break, % | 10 | |
| 63 |
| Poisson's Ratio | 0.33 | |
| 0.25 |
| Shear Modulus, GPa | 53 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 1210 | |
| 140 |
| Tensile Strength: Yield (Proof), MPa | 550 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 310 | |
| 90 |
| Melting Completion (Liquidus), °C | 1170 | |
| 410 |
| Melting Onset (Solidus), °C | 1110 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Conductivity, W/m-K | 30 | |
| 110 |
| Thermal Expansion, µm/m-K | 15 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 90 | |
| 11 |
| Density, g/cm3 | 8.8 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 9.5 | |
| 2.8 |
| Embodied Energy, MJ/kg | 140 | |
| 53 |
| Embodied Water, L/kg | 280 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 99 | |
| 85 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1080 | |
| 81 |
| Stiffness to Weight: Axial, points | 8.9 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 20 | |
| 23 |
| Strength to Weight: Axial, points | 38 | |
| 6.1 |
| Strength to Weight: Bending, points | 29 | |
| 9.3 |
| Thermal Diffusivity, mm2/s | 8.5 | |
| 44 |
| Thermal Shock Resistance, points | 40 | |
| 4.6 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0020 |
| Beryllium (Be), % | 1.1 to 1.2 | |
| 0 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Copper (Cu), % | 62.4 to 68.8 | |
| 0 to 0.0050 |
| Iron (Fe), % | 0.4 to 1.0 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 to 0.010 | |
| 0.030 to 0.080 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.0015 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 0 to 0.015 |
| Nickel (Ni), % | 29 to 33 | |
| 0 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 |
| Titanium (Ti), % | 0.15 to 0.35 | |
| 0 to 0.020 |
| Zinc (Zn), % | 0 | |
| 99.862 to 100 |
| Zirconium (Zr), % | 0.15 to 0.35 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |