C96900 Copper-nickel vs. AWS E409Nb
C96900 copper-nickel belongs to the copper alloys classification, while AWS E409Nb belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C96900 copper-nickel and the bottom bar is AWS E409Nb.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 4.5 | |
| 23 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 45 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 850 | |
| 500 |
| Tensile Strength: Yield (Proof), MPa | 830 | |
| 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 280 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1460 |
| Melting Onset (Solidus), °C | 960 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 480 |
| Thermal Expansion, µm/m-K | 17 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.2 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 39 | |
| 13 |
| Density, g/cm3 | 8.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.6 | |
| 2.9 |
| Embodied Energy, MJ/kg | 72 | |
| 42 |
| Embodied Water, L/kg | 360 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 38 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2820 | |
| 380 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 27 | |
| 18 |
| Strength to Weight: Bending, points | 23 | |
| 18 |
| Thermal Shock Resistance, points | 30 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.12 |
| Chromium (Cr), % | 0 | |
| 11 to 14 |
| Copper (Cu), % | 73.6 to 78 | |
| 0 to 0.75 |
| Iron (Fe), % | 0 to 0.5 | |
| 80.2 to 88.5 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.15 | |
| 0 |
| Manganese (Mn), % | 0.050 to 0.3 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.75 |
| Nickel (Ni), % | 14.5 to 15.5 | |
| 0 to 0.6 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0.5 to 1.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 7.5 to 8.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |