C96900 Copper-nickel vs. C46400 Brass
Both C96900 copper-nickel and C46400 brass are copper alloys. They have 62% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C96900 copper-nickel and the bottom bar is C46400 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 4.5 | |
| 17 to 40 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 45 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 850 | |
| 400 to 500 |
| Tensile Strength: Yield (Proof), MPa | 830 | |
| 160 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 120 |
| Melting Completion (Liquidus), °C | 1060 | |
| 900 |
| Melting Onset (Solidus), °C | 960 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.2 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 39 | |
| 23 |
| Density, g/cm3 | 8.8 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 4.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 72 | |
| 47 |
| Embodied Water, L/kg | 360 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 38 | |
| 76 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2820 | |
| 120 to 500 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 27 | |
| 14 to 17 |
| Strength to Weight: Bending, points | 23 | |
| 15 to 17 |
| Thermal Shock Resistance, points | 30 | |
| 13 to 16 |
Alloy Composition
| Copper (Cu), % | 73.6 to 78 | |
| 59 to 62 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 to 0.2 |
| Magnesium (Mg), % | 0 to 0.15 | |
| 0 |
| Manganese (Mn), % | 0.050 to 0.3 | |
| 0 |
| Nickel (Ni), % | 14.5 to 15.5 | |
| 0 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 |
| Tin (Sn), % | 7.5 to 8.5 | |
| 0.5 to 1.0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 36.3 to 40.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |