MakeItFrom.com
Menu (ESC)

C97800 Nickel Silver vs. ASTM A369 Grade FP2

C97800 nickel silver belongs to the copper alloys classification, while ASTM A369 grade FP2 belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C97800 nickel silver and the bottom bar is ASTM A369 grade FP2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 130
190
Elongation at Break, % 10
20
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 48
73
Tensile Strength: Ultimate (UTS), MPa 370
430
Tensile Strength: Yield (Proof), MPa 170
240

Thermal Properties

Latent Heat of Fusion, J/g 220
250
Maximum Temperature: Mechanical, °C 230
420
Melting Completion (Liquidus), °C 1180
1470
Melting Onset (Solidus), °C 1140
1430
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 25
49
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.0
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 40
2.6
Density, g/cm3 8.8
7.9
Embodied Carbon, kg CO2/kg material 5.1
1.6
Embodied Energy, MJ/kg 76
20
Embodied Water, L/kg 330
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
75
Resilience: Unit (Modulus of Resilience), kJ/m3 120
150
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 12
15
Strength to Weight: Bending, points 13
16
Thermal Diffusivity, mm2/s 7.3
13
Thermal Shock Resistance, points 13
13

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.2
0
Carbon (C), % 0
0.1 to 0.2
Chromium (Cr), % 0
0.5 to 0.81
Copper (Cu), % 64 to 67
0
Iron (Fe), % 0 to 1.5
97.4 to 98.6
Lead (Pb), % 1.0 to 2.5
0
Manganese (Mn), % 0
0.3 to 0.61
Molybdenum (Mo), % 0
0.44 to 0.65
Nickel (Ni), % 24 to 27
0
Phosphorus (P), % 0 to 0.050
0 to 0.025
Silicon (Si), % 0 to 0.15
0.1 to 0.3
Sulfur (S), % 0 to 0.080
0 to 0.025
Tin (Sn), % 4.0 to 5.5
0
Zinc (Zn), % 1.0 to 4.0
0
Residuals, % 0 to 0.4
0