C97800 Nickel Silver vs. EN 1.0234 Steel
C97800 nickel silver belongs to the copper alloys classification, while EN 1.0234 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C97800 nickel silver and the bottom bar is EN 1.0234 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 190 |
| Elongation at Break, % | 10 | |
| 12 to 29 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 48 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 370 | |
| 350 to 480 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 220 to 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 400 |
| Melting Completion (Liquidus), °C | 1180 | |
| 1460 |
| Melting Onset (Solidus), °C | 1140 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 25 | |
| 53 |
| Thermal Expansion, µm/m-K | 16 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.0 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.1 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 40 | |
| 1.8 |
| Density, g/cm3 | 8.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 76 | |
| 18 |
| Embodied Water, L/kg | 330 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 | |
| 36 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 | |
| 130 to 440 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 12 | |
| 12 to 17 |
| Strength to Weight: Bending, points | 13 | |
| 14 to 17 |
| Thermal Diffusivity, mm2/s | 7.3 | |
| 14 |
| Thermal Shock Resistance, points | 13 | |
| 11 to 15 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0.020 to 0.060 |
| Antimony (Sb), % | 0 to 0.2 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.13 to 0.17 |
| Copper (Cu), % | 64 to 67 | |
| 0 |
| Iron (Fe), % | 0 to 1.5 | |
| 99.02 to 99.5 |
| Lead (Pb), % | 1.0 to 2.5 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.35 to 0.6 |
| Nickel (Ni), % | 24 to 27 | |
| 0 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.080 | |
| 0 to 0.025 |
| Tin (Sn), % | 4.0 to 5.5 | |
| 0 |
| Zinc (Zn), % | 1.0 to 4.0 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |