C97800 Nickel Silver vs. Grade 11 Titanium

C97800 nickel silver belongs to the copper alloys classification, while grade 11 titanium belongs to the titanium alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is C97800 nickel silver and the bottom bar is grade 11 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 130
110
Elongation at Break, % 10
29
Poisson's Ratio 0.33
0.32
Shear Modulus, GPa 48
38
Tensile Strength: Ultimate (UTS), MPa 370
310
Tensile Strength: Yield (Proof), MPa 170
230

Thermal Properties

Latent Heat of Fusion, J/g 220
420
Maximum Temperature: Mechanical, °C 230
320
Melting Completion (Liquidus), °C 1180
1660
Melting Onset (Solidus), °C 1140
1610
Specific Heat Capacity, J/kg-K 390
540
Thermal Conductivity, W/m-K 25
22
Thermal Expansion, µm/m-K 16
9.2

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.0
3.7
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
7.3

Otherwise Unclassified Properties

Density, g/cm3 8.8
4.5
Embodied Carbon, kg CO2/kg material 5.1
47
Embodied Energy, MJ/kg 76
800
Embodied Water, L/kg 330
470

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
81
Resilience: Unit (Modulus of Resilience), kJ/m3 120
240
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 19
35
Strength to Weight: Axial, points 12
19
Strength to Weight: Bending, points 13
22
Thermal Diffusivity, mm2/s 7.3
8.9
Thermal Shock Resistance, points 13
22

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.2
0
Carbon (C), % 0
0 to 0.080
Copper (Cu), % 64 to 67
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 0 to 1.5
0 to 0.2
Lead (Pb), % 1.0 to 2.5
0
Nickel (Ni), % 24 to 27
0
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.18
Palladium (Pd), % 0
0.12 to 0.25
Phosphorus (P), % 0 to 0.050
0
Silicon (Si), % 0 to 0.15
0
Sulfur (S), % 0 to 0.080
0
Tin (Sn), % 4.0 to 5.5
0
Titanium (Ti), % 0
98.8 to 99.88
Zinc (Zn), % 1.0 to 4.0
0
Residuals, % 0
0 to 0.4