C99600 Bronze vs. C24000 Brass
Both C99600 bronze and C24000 brass are copper alloys. They have 56% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is C99600 bronze and the bottom bar is C24000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 150 | |
| 110 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 56 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 560 | |
| 310 to 640 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 160 |
| Melting Completion (Liquidus), °C | 1100 | |
| 1000 |
| Melting Onset (Solidus), °C | 1050 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 390 |
| Thermal Expansion, µm/m-K | 19 | |
| 19 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 22 | |
| 27 |
| Density, g/cm3 | 8.1 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 2.6 |
| Embodied Energy, MJ/kg | 51 | |
| 43 |
| Embodied Water, L/kg | 300 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 10 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 22 | |
| 19 |
| Strength to Weight: Axial, points | 19 | |
| 10 to 21 |
| Strength to Weight: Bending, points | 19 | |
| 12 to 20 |
| Thermal Shock Resistance, points | 14 | |
| 10 to 22 |
Alloy Composition
| Aluminum (Al), % | 1.0 to 2.8 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Cobalt (Co), % | 0 to 0.2 | |
| 0 |
| Copper (Cu), % | 50.8 to 60 | |
| 78.5 to 81.5 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 to 0.050 |
| Manganese (Mn), % | 39 to 45 | |
| 0 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 18.2 to 21.5 |
| Residuals, % | 0 | |
| 0 to 0.2 |