K93050 Alloy vs. N07041 Nickel
K93050 alloy belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 11 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is K93050 alloy and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 680 | |
| 1400 |
Thermal Properties
| Melting Onset (Solidus), °C | 1380 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 450 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 17 to 23 | |
| 47 |
| Strength to Weight: Bending, points | 17 to 21 | |
| 34 |
| Thermal Shock Resistance, points | 16 to 21 | |
| 38 |