K93500 Alloy vs. C15500 Copper
K93500 alloy belongs to the iron alloys classification, while C15500 copper belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is K93500 alloy and the bottom bar is C15500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Poisson's Ratio | 0.3 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 490 to 810 | |
| 280 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 210 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1080 |
| Melting Onset (Solidus), °C | 1380 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 390 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 33 |
| Density, g/cm3 | 8.2 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 4.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 65 | |
| 42 |
| Embodied Water, L/kg | 130 | |
| 360 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 23 | |
| 18 |
| Strength to Weight: Axial, points | 17 to 27 | |
| 8.6 to 17 |
| Strength to Weight: Bending, points | 17 to 23 | |
| 11 to 17 |
| Thermal Shock Resistance, points | 15 to 25 | |
| 9.8 to 20 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.1 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 0 to 0.25 | |
| 0 |
| Cobalt (Co), % | 5.0 | |
| 0 |
| Copper (Cu), % | 0 | |
| 99.75 to 99.853 |
| Iron (Fe), % | 61.4 to 63 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.1 | |
| 0.080 to 0.13 |
| Manganese (Mn), % | 0 to 0.6 | |
| 0 |
| Nickel (Ni), % | 32 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0.040 to 0.080 |
| Silicon (Si), % | 0 to 0.25 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0.027 to 0.1 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.1 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |