K93500 Alloy vs. Z21210 Zinc
K93500 alloy belongs to the iron alloys classification, while Z21210 zinc belongs to the zinc alloys. There are 8 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is K93500 alloy and the bottom bar is Z21210 zinc.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 8.2 | |
| 7.1 |
| Melting Completion (Liquidus), °C | 1430 | |
| 420 |
| Melting Onset (Solidus), °C | 1380 | |
| 420 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 400 |
| Strength to Weight: Axial, points | 17 to 27 | |
| 5.7 to 6.4 |
| Strength to Weight: Bending, points | 17 to 23 | |
| 8.6 to 9.4 |
| Tensile Strength: Ultimate (UTS), MPa | 490 to 810 | |
| 150 to 170 |
| Thermal Expansion, µm/m-K | 12 | |
| 32 |