K93600 Alloy vs. ASTM A514 Steel
Both K93600 alloy and ASTM A514 steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is ASTM A514 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
190 |
Elongation at Break, % | 5.0 to 35 | |
18 to 21 |
Shear Strength, MPa | 320 to 380 | |
490 to 520 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
790 to 830 |
Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
690 to 770 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 440 | |
400 to 440 |
Melting Onset (Solidus), °C | 1430 | |
1420 |
Specific Heat Capacity, J/kg-K | 520 | |
470 |
Thermal Conductivity, W/m-K | 13 | |
37 to 51 |
Thermal Expansion, µm/m-K | 7.3 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
7.2 to 7.6 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
8.3 to 8.8 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
7.8 to 7.9 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
140 to 170 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
1280 to 1590 |
Stiffness to Weight: Axial, points | 9.4 | |
13 |
Stiffness to Weight: Bending, points | 21 | |
24 |
Strength to Weight: Axial, points | 16 to 28 | |
28 to 29 |
Strength to Weight: Bending, points | 17 to 24 | |
24 to 25 |
Thermal Diffusivity, mm2/s | 3.1 | |
10 to 14 |
Thermal Shock Resistance, points | 34 to 57 | |
23 to 24 |