K93600 Alloy vs. AWS E80C-W2
Both K93600 alloy and AWS E80C-W2 are iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is AWS E80C-W2.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
190 |
Elongation at Break, % | 5.0 to 35 | |
25 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
620 |
Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
540 |
Thermal Properties
Melting Onset (Solidus), °C | 1430 | |
1410 |
Specific Heat Capacity, J/kg-K | 520 | |
470 |
Thermal Conductivity, W/m-K | 13 | |
39 |
Thermal Expansion, µm/m-K | 7.3 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
7.5 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
8.7 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
7.8 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
150 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
770 |
Stiffness to Weight: Axial, points | 9.4 | |
13 |
Stiffness to Weight: Bending, points | 21 | |
24 |
Strength to Weight: Axial, points | 16 to 28 | |
22 |
Strength to Weight: Bending, points | 17 to 24 | |
21 |
Thermal Diffusivity, mm2/s | 3.1 | |
10 |
Thermal Shock Resistance, points | 34 to 57 | |
18 |