K93600 Alloy vs. EN 1.3543 Stainless Steel
Both K93600 alloy and EN 1.3543 stainless steel are iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.3543 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
200 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
730 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 440 | |
870 |
Melting Onset (Solidus), °C | 1430 | |
1390 |
Specific Heat Capacity, J/kg-K | 520 | |
480 |
Thermal Conductivity, W/m-K | 13 | |
22 |
Thermal Expansion, µm/m-K | 7.3 | |
10 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
2.5 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
3.0 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
7.7 |
Common Calculations
Stiffness to Weight: Axial, points | 9.4 | |
14 |
Stiffness to Weight: Bending, points | 21 | |
25 |
Strength to Weight: Axial, points | 16 to 28 | |
27 |
Strength to Weight: Bending, points | 17 to 24 | |
24 |
Thermal Diffusivity, mm2/s | 3.1 | |
6.1 |
Thermal Shock Resistance, points | 34 to 57 | |
26 |