K93600 Alloy vs. EN 1.4307 Stainless Steel
Both K93600 alloy and EN 1.4307 stainless steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.4307 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Elongation at Break, % | 5.0 to 35 | |
| 14 to 46 |
| Shear Strength, MPa | 320 to 380 | |
| 410 to 550 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 590 to 900 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 200 to 570 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 440 | |
| 940 |
| Melting Onset (Solidus), °C | 1430 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 480 |
| Thermal Conductivity, W/m-K | 13 | |
| 15 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 2.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 110 to 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 100 to 810 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 21 to 32 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 20 to 27 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 4.0 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 13 to 20 |