K93600 Alloy vs. SAE-AISI D2 Steel
Both K93600 alloy and SAE-AISI D2 steel are iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is SAE-AISI D2 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
190 |
Elongation at Break, % | 5.0 to 35 | |
5.0 to 16 |
Shear Strength, MPa | 320 to 380 | |
460 to 1160 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
760 to 2000 |
Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
470 to 1510 |
Thermal Properties
Melting Onset (Solidus), °C | 1430 | |
1390 |
Specific Heat Capacity, J/kg-K | 520 | |
480 |
Thermal Conductivity, W/m-K | 13 | |
31 |
Thermal Expansion, µm/m-K | 7.3 | |
11 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
4.3 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
5.1 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
7.7 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
92 to 100 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
570 to 5940 |
Stiffness to Weight: Axial, points | 9.4 | |
14 |
Stiffness to Weight: Bending, points | 21 | |
25 |
Strength to Weight: Axial, points | 16 to 28 | |
27 to 72 |
Strength to Weight: Bending, points | 17 to 24 | |
24 to 46 |
Thermal Diffusivity, mm2/s | 3.1 | |
8.3 |
Thermal Shock Resistance, points | 34 to 57 | |
25 to 67 |