K93600 Alloy vs. SAE-AISI T8 Steel
Both K93600 alloy and SAE-AISI T8 steel are iron alloys. There are 13 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is SAE-AISI T8 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
200 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
780 to 2140 |
Thermal Properties
Melting Onset (Solidus), °C | 1430 | |
1670 |
Specific Heat Capacity, J/kg-K | 520 | |
420 |
Thermal Conductivity, W/m-K | 13 | |
18 |
Thermal Expansion, µm/m-K | 7.3 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
9.0 |
Common Calculations
Stiffness to Weight: Axial, points | 9.4 | |
12 |
Stiffness to Weight: Bending, points | 21 | |
22 |
Strength to Weight: Axial, points | 16 to 28 | |
24 to 66 |
Strength to Weight: Bending, points | 17 to 24 | |
21 to 41 |
Thermal Diffusivity, mm2/s | 3.1 | |
4.8 |
Thermal Shock Resistance, points | 34 to 57 | |
24 to 66 |