K93600 Alloy vs. C55281 Copper
K93600 alloy belongs to the iron alloys classification, while C55281 copper belongs to the copper alloys. There are 12 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is C55281 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 110 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 190 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 440 | |
| 200 |
| Melting Onset (Solidus), °C | 1430 | |
| 640 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 400 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.4 | |
| 6.9 |
| Stiffness to Weight: Bending, points | 21 | |
| 18 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 6.1 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 8.5 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 7.7 |