K93600 Alloy vs. K93050 Alloy
Both K93600 alloy and K93050 alloy are iron alloys. There are 11 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is K93050 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 190 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 500 to 680 |
Thermal Properties
| Melting Onset (Solidus), °C | 1430 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 460 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 23 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 17 to 23 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 17 to 21 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 16 to 21 |