K93600 Alloy vs. N06230 Nickel

K93600 alloy belongs to the iron alloys classification, while N06230 nickel belongs to the nickel alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is K93600 alloy and the bottom bar is N06230 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
210
Elongation at Break, % 5.0 to 35
38 to 48
Shear Strength, MPa 320 to 380
420 to 600
Tensile Strength: Ultimate (UTS), MPa 480 to 810
620 to 840
Tensile Strength: Yield (Proof), MPa 280 to 750
330 to 400

Thermal Properties

Maximum Temperature: Mechanical, °C 440
990
Melting Onset (Solidus), °C 1430
1300
Specific Heat Capacity, J/kg-K 520
420
Thermal Conductivity, W/m-K 13
8.9
Thermal Expansion, µm/m-K 7.3
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
1.3

Otherwise Unclassified Properties

Density, g/cm3 8.1
9.5

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 280
200 to 330
Resilience: Unit (Modulus of Resilience), kJ/m3 280 to 2050
250 to 380
Stiffness to Weight: Axial, points 9.4
12
Stiffness to Weight: Bending, points 21
21
Strength to Weight: Axial, points 16 to 28
18 to 25
Strength to Weight: Bending, points 17 to 24
17 to 21
Thermal Diffusivity, mm2/s 3.1
2.3
Thermal Shock Resistance, points 34 to 57
17 to 23