K93600 Alloy vs. S21904 Stainless Steel
Both K93600 alloy and S21904 stainless steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is S21904 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Elongation at Break, % | 5.0 to 35 | |
| 17 to 51 |
| Shear Strength, MPa | 320 to 380 | |
| 510 to 620 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 700 to 1000 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 390 to 910 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 440 | |
| 980 |
| Melting Onset (Solidus), °C | 1430 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 480 |
| Thermal Conductivity, W/m-K | 13 | |
| 14 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 2.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.7 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 160 to 310 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
| 380 to 2070 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 25 to 36 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 23 to 29 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 3.8 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 15 to 21 |