K93603 Alloy vs. R30012 Cobalt

K93603 alloy belongs to the iron alloys classification, while R30012 cobalt belongs to the cobalt alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is K93603 alloy and the bottom bar is R30012 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Poisson's Ratio 0.3
0.28
Shear Modulus, GPa 72
86
Tensile Strength: Ultimate (UTS), MPa 490 to 810
830

Thermal Properties

Latent Heat of Fusion, J/g 270
320
Melting Completion (Liquidus), °C 1430
1470
Melting Onset (Solidus), °C 1380
1280
Specific Heat Capacity, J/kg-K 460
440
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Density, g/cm3 8.2
8.8
Embodied Carbon, kg CO2/kg material 4.8
8.3
Embodied Energy, MJ/kg 66
120
Embodied Water, L/kg 120
480

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 17 to 27
26
Strength to Weight: Bending, points 17 to 24
22
Thermal Shock Resistance, points 15 to 25
23

Alloy Composition

Aluminum (Al), % 0 to 0.1
0
Carbon (C), % 0 to 0.050
1.4 to 2.0
Chromium (Cr), % 0 to 0.25
27 to 32
Cobalt (Co), % 0 to 0.5
47.5 to 64.1
Iron (Fe), % 61.8 to 64
0 to 3.0
Magnesium (Mg), % 0 to 0.1
0
Manganese (Mn), % 0 to 0.6
0
Molybdenum (Mo), % 0
0 to 1.0
Nickel (Ni), % 36
0 to 3.0
Phosphorus (P), % 0 to 0.015
0
Silicon (Si), % 0 to 0.4
0 to 2.0
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0 to 0.1
0
Tungsten (W), % 0
7.5 to 9.5
Zirconium (Zr), % 0 to 0.1
0