K94200 Alloy vs. EN 1.1165 Cast Steel
Both K94200 alloy and EN 1.1165 cast steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is K94200 alloy and the bottom bar is EN 1.1165 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 190 |
| Elongation at Break, % | 5.0 to 32 | |
| 11 to 20 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 54 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 710 | |
| 600 to 780 |
| Tensile Strength: Yield (Proof), MPa | 270 to 650 | |
| 290 to 620 |
Thermal Properties
| Melting Onset (Solidus), °C | 1440 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 470 |
| Thermal Conductivity, W/m-K | 15 | |
| 51 |
| Thermal Expansion, µm/m-K | 5.0 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.7 | |
| 7.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.0 | |
| 8.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 35 to 130 | |
| 81 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 1460 | |
| 230 to 1010 |
| Stiffness to Weight: Axial, points | 9.8 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 17 to 24 | |
| 21 to 28 |
| Strength to Weight: Bending, points | 17 to 22 | |
| 20 to 24 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 14 |
| Thermal Shock Resistance, points | 49 to 70 | |
| 19 to 25 |