K94200 Alloy vs. Nickel 201
K94200 alloy belongs to the iron alloys classification, while nickel 201 belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is K94200 alloy and the bottom bar is nickel 201.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 180 |
| Elongation at Break, % | 5.0 to 32 | |
| 4.5 to 45 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 54 | |
| 70 |
| Shear Strength, MPa | 330 to 410 | |
| 270 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 710 | |
| 390 to 660 |
| Tensile Strength: Yield (Proof), MPa | 270 to 650 | |
| 80 to 510 |
Thermal Properties
| Curie Temperature, °C | 350 | |
| 360 |
| Melting Onset (Solidus), °C | 1440 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 440 |
| Thermal Conductivity, W/m-K | 15 | |
| 78 |
| Thermal Expansion, µm/m-K | 5.0 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.7 | |
| 19 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.0 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 35 to 130 | |
| 25 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 1460 | |
| 17 to 720 |
| Stiffness to Weight: Axial, points | 9.8 | |
| 11 |
| Stiffness to Weight: Bending, points | 21 | |
| 21 |
| Strength to Weight: Axial, points | 17 to 24 | |
| 12 to 20 |
| Strength to Weight: Bending, points | 17 to 22 | |
| 13 to 19 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 20 |
| Thermal Shock Resistance, points | 49 to 70 | |
| 11 to 19 |