K94200 Alloy vs. SAE-AISI M3 Class 2 Steel
Both K94200 alloy and SAE-AISI M3 class 2 steel are iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is K94200 alloy and the bottom bar is SAE-AISI M3 class 2 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
200 |
Poisson's Ratio | 0.34 | |
0.29 |
Shear Modulus, GPa | 54 | |
77 |
Tensile Strength: Ultimate (UTS), MPa | 500 to 710 | |
770 to 2210 |
Thermal Properties
Melting Onset (Solidus), °C | 1440 | |
1570 |
Specific Heat Capacity, J/kg-K | 500 | |
440 |
Thermal Conductivity, W/m-K | 15 | |
26 |
Thermal Expansion, µm/m-K | 5.0 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.2 | |
8.3 |
Common Calculations
Stiffness to Weight: Axial, points | 9.8 | |
13 |
Stiffness to Weight: Bending, points | 21 | |
23 |
Strength to Weight: Axial, points | 17 to 24 | |
26 to 74 |
Strength to Weight: Bending, points | 17 to 22 | |
22 to 45 |
Thermal Diffusivity, mm2/s | 3.7 | |
7.2 |
Thermal Shock Resistance, points | 49 to 70 | |
24 to 69 |