K94200 Alloy vs. C63800 Bronze
K94200 alloy belongs to the iron alloys classification, while C63800 bronze belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is K94200 alloy and the bottom bar is C63800 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 110 |
| Elongation at Break, % | 5.0 to 32 | |
| 7.9 to 41 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 54 | |
| 43 |
| Shear Strength, MPa | 330 to 410 | |
| 320 to 500 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 710 | |
| 460 to 1010 |
Thermal Properties
| Melting Onset (Solidus), °C | 1440 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 410 |
| Thermal Conductivity, W/m-K | 15 | |
| 40 |
| Thermal Expansion, µm/m-K | 5.0 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.7 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.0 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.8 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 21 | |
| 19 |
| Strength to Weight: Axial, points | 17 to 24 | |
| 15 to 33 |
| Strength to Weight: Bending, points | 17 to 22 | |
| 15 to 26 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 11 |
| Thermal Shock Resistance, points | 49 to 70 | |
| 17 to 36 |