K94200 Alloy vs. K93600 Alloy
Both K94200 alloy and K93600 alloy are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is K94200 alloy and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 140 |
| Elongation at Break, % | 5.0 to 32 | |
| 5.0 to 35 |
| Shear Strength, MPa | 330 to 410 | |
| 320 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 710 | |
| 480 to 810 |
| Tensile Strength: Yield (Proof), MPa | 270 to 650 | |
| 280 to 750 |
Thermal Properties
| Curie Temperature, °C | 350 | |
| 250 |
| Melting Onset (Solidus), °C | 1440 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 520 |
| Thermal Conductivity, W/m-K | 15 | |
| 13 |
| Thermal Expansion, µm/m-K | 5.0 | |
| 7.3 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.7 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.0 | |
| 2.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.1 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 35 to 130 | |
| 21 to 280 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 1460 | |
| 280 to 2050 |
| Stiffness to Weight: Axial, points | 9.8 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 21 | |
| 21 |
| Strength to Weight: Axial, points | 17 to 24 | |
| 16 to 28 |
| Strength to Weight: Bending, points | 17 to 22 | |
| 17 to 24 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 3.1 |
| Thermal Shock Resistance, points | 49 to 70 | |
| 34 to 57 |