K94200 Alloy vs. S17600 Stainless Steel
Both K94200 alloy and S17600 stainless steel are iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is K94200 alloy and the bottom bar is S17600 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Elongation at Break, % | 5.0 to 32 | |
| 8.6 to 11 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 54 | |
| 76 |
| Shear Strength, MPa | 330 to 410 | |
| 560 to 880 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 710 | |
| 940 to 1490 |
| Tensile Strength: Yield (Proof), MPa | 270 to 650 | |
| 580 to 1310 |
Thermal Properties
| Melting Onset (Solidus), °C | 1440 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 480 |
| Thermal Conductivity, W/m-K | 15 | |
| 15 |
| Thermal Expansion, µm/m-K | 5.0 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.7 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.0 | |
| 2.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 35 to 130 | |
| 70 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 1460 | |
| 850 to 4390 |
| Stiffness to Weight: Axial, points | 9.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 17 to 24 | |
| 34 to 54 |
| Strength to Weight: Bending, points | 17 to 22 | |
| 28 to 37 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 4.1 |
| Thermal Shock Resistance, points | 49 to 70 | |
| 31 to 50 |