K94200 Alloy vs. S33228 Stainless Steel
Both K94200 alloy and S33228 stainless steel are iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is K94200 alloy and the bottom bar is S33228 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Elongation at Break, % | 5.0 to 32 | |
| 34 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 54 | |
| 79 |
| Shear Strength, MPa | 330 to 410 | |
| 380 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 710 | |
| 570 |
| Tensile Strength: Yield (Proof), MPa | 270 to 650 | |
| 210 |
Thermal Properties
| Melting Onset (Solidus), °C | 1440 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 470 |
| Thermal Expansion, µm/m-K | 5.0 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.0 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 35 to 130 | |
| 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 1460 | |
| 110 |
| Stiffness to Weight: Axial, points | 9.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 17 to 24 | |
| 20 |
| Strength to Weight: Bending, points | 17 to 22 | |
| 19 |
| Thermal Shock Resistance, points | 49 to 70 | |
| 13 |