N06002 Nickel vs. EN 2.4668 Nickel

Both N06002 nickel and EN 2.4668 nickel are nickel alloys. They have 89% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is N06002 nickel and the bottom bar is EN 2.4668 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 41
14
Fatigue Strength, MPa 250
590
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 81
75
Shear Strength, MPa 520
840
Tensile Strength: Ultimate (UTS), MPa 760
1390
Tensile Strength: Yield (Proof), MPa 310
1160

Thermal Properties

Latent Heat of Fusion, J/g 320
310
Maximum Temperature: Mechanical, °C 990
980
Melting Completion (Liquidus), °C 1360
1460
Melting Onset (Solidus), °C 1260
1410
Specific Heat Capacity, J/kg-K 450
450
Thermal Conductivity, W/m-K 9.9
13
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.6
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 55
75
Density, g/cm3 8.5
8.3
Embodied Carbon, kg CO2/kg material 9.3
13
Embodied Energy, MJ/kg 130
190
Embodied Water, L/kg 270
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 250
180
Resilience: Unit (Modulus of Resilience), kJ/m3 230
3490
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 25
46
Strength to Weight: Bending, points 22
33
Thermal Diffusivity, mm2/s 2.6
3.5
Thermal Shock Resistance, points 19
40

Alloy Composition

Aluminum (Al), % 0
0.3 to 0.7
Boron (B), % 0
0.0020 to 0.0060
Carbon (C), % 0.050 to 0.15
0.020 to 0.080
Chromium (Cr), % 20.5 to 23
17 to 21
Cobalt (Co), % 0.5 to 2.5
0 to 1.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 17 to 20
11.2 to 24.6
Manganese (Mn), % 0 to 1.0
0 to 0.35
Molybdenum (Mo), % 8.0 to 10
2.8 to 3.3
Nickel (Ni), % 42.3 to 54
50 to 55
Niobium (Nb), % 0
4.7 to 5.5
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.6 to 1.2
Tungsten (W), % 0.2 to 1.0
0