N06002 Nickel vs. S39277 Stainless Steel
N06002 nickel belongs to the nickel alloys classification, while S39277 stainless steel belongs to the iron alloys. They have 52% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is N06002 nickel and the bottom bar is S39277 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 200 |
| Elongation at Break, % | 41 | |
| 28 |
| Fatigue Strength, MPa | 250 | |
| 480 |
| Poisson's Ratio | 0.28 | |
| 0.27 |
| Shear Modulus, GPa | 81 | |
| 80 |
| Shear Strength, MPa | 520 | |
| 600 |
| Tensile Strength: Ultimate (UTS), MPa | 760 | |
| 930 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 660 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 990 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1460 |
| Melting Onset (Solidus), °C | 1260 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 9.9 | |
| 16 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.5 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.6 | |
| 2.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 55 | |
| 23 |
| Density, g/cm3 | 8.5 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 9.3 | |
| 4.2 |
| Embodied Energy, MJ/kg | 130 | |
| 59 |
| Embodied Water, L/kg | 270 | |
| 180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 250 | |
| 240 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 | |
| 1070 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 25 | |
| 33 |
| Strength to Weight: Bending, points | 22 | |
| 27 |
| Thermal Diffusivity, mm2/s | 2.6 | |
| 4.2 |
| Thermal Shock Resistance, points | 19 | |
| 26 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.15 | |
| 0 to 0.025 |
| Chromium (Cr), % | 20.5 to 23 | |
| 24 to 26 |
| Cobalt (Co), % | 0.5 to 2.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 1.2 to 2.0 |
| Iron (Fe), % | 17 to 20 | |
| 56.8 to 64.3 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.8 |
| Molybdenum (Mo), % | 8.0 to 10 | |
| 3.0 to 4.0 |
| Nickel (Ni), % | 42.3 to 54 | |
| 6.5 to 8.0 |
| Nitrogen (N), % | 0 | |
| 0.23 to 0.33 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.8 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.0020 |
| Tungsten (W), % | 0.2 to 1.0 | |
| 0.8 to 1.2 |