N06007 Nickel vs. EN 1.1192 Steel
N06007 nickel belongs to the nickel alloys classification, while EN 1.1192 steel belongs to the iron alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is N06007 nickel and the bottom bar is EN 1.1192 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 79 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 520 to 1810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 990 | |
| 400 |
| Melting Completion (Liquidus), °C | 1340 | |
| 1460 |
| Melting Onset (Solidus), °C | 1260 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 10 | |
| 51 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 1.8 |
| Density, g/cm3 | 8.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 1.4 |
| Embodied Energy, MJ/kg | 140 | |
| 19 |
| Embodied Water, L/kg | 260 | |
| 46 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 23 | |
| 18 to 64 |
| Strength to Weight: Bending, points | 21 | |
| 18 to 42 |
| Thermal Diffusivity, mm2/s | 2.7 | |
| 14 |
| Thermal Shock Resistance, points | 18 | |
| 16 to 58 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0.42 to 0.5 |
| Chromium (Cr), % | 21 to 23.5 | |
| 0 |
| Cobalt (Co), % | 0 to 2.5 | |
| 0 |
| Copper (Cu), % | 1.5 to 2.5 | |
| 0 to 0.25 |
| Iron (Fe), % | 18 to 21 | |
| 98.1 to 99.08 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 5.5 to 7.5 | |
| 0 |
| Nickel (Ni), % | 36.1 to 51.1 | |
| 0 |
| Niobium (Nb), % | 1.8 to 2.5 | |
| 0 |
| Nitrogen (N), % | 0.15 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |
| Tungsten (W), % | 0 to 1.0 | |
| 0 |