N06007 Nickel vs. Titanium 15-3-3-3
N06007 nickel belongs to the nickel alloys classification, while titanium 15-3-3-3 belongs to the titanium alloys. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is N06007 nickel and the bottom bar is titanium 15-3-3-3.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 100 |
| Elongation at Break, % | 38 | |
| 5.7 to 8.0 |
| Fatigue Strength, MPa | 330 | |
| 610 to 710 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 79 | |
| 39 |
| Shear Strength, MPa | 470 | |
| 660 to 810 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 1120 to 1390 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 1100 to 1340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 990 | |
| 430 |
| Melting Completion (Liquidus), °C | 1340 | |
| 1620 |
| Melting Onset (Solidus), °C | 1260 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 520 |
| Thermal Conductivity, W/m-K | 10 | |
| 8.1 |
| Thermal Expansion, µm/m-K | 14 | |
| 9.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 40 |
| Density, g/cm3 | 8.4 | |
| 4.8 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 59 |
| Embodied Energy, MJ/kg | 140 | |
| 950 |
| Embodied Water, L/kg | 260 | |
| 260 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 | |
| 78 to 89 |
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 23 | |
| 32 |
| Strength to Weight: Axial, points | 23 | |
| 64 to 80 |
| Strength to Weight: Bending, points | 21 | |
| 50 to 57 |
| Thermal Diffusivity, mm2/s | 2.7 | |
| 3.2 |
| Thermal Shock Resistance, points | 18 | |
| 79 to 98 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 2.5 to 3.5 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.050 |
| Chromium (Cr), % | 21 to 23.5 | |
| 2.5 to 3.5 |
| Cobalt (Co), % | 0 to 2.5 | |
| 0 |
| Copper (Cu), % | 1.5 to 2.5 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 18 to 21 | |
| 0 to 0.25 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0 |
| Molybdenum (Mo), % | 5.5 to 7.5 | |
| 0 |
| Nickel (Ni), % | 36.1 to 51.1 | |
| 0 |
| Niobium (Nb), % | 1.8 to 2.5 | |
| 0 |
| Nitrogen (N), % | 0.15 to 0.25 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.13 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 2.5 to 3.5 |
| Titanium (Ti), % | 0 | |
| 72.6 to 78.5 |
| Tungsten (W), % | 0 to 1.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 14 to 16 |
| Residuals, % | 0 | |
| 0 to 0.4 |