N06025 Nickel vs. S20161 Stainless Steel
N06025 nickel belongs to the nickel alloys classification, while S20161 stainless steel belongs to the iron alloys. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is N06025 nickel and the bottom bar is S20161 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 32 | |
| 46 |
| Fatigue Strength, MPa | 220 | |
| 360 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 76 |
| Shear Strength, MPa | 500 | |
| 690 |
| Tensile Strength: Ultimate (UTS), MPa | 760 | |
| 980 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 870 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1380 |
| Melting Onset (Solidus), °C | 1300 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 490 |
| Thermal Conductivity, W/m-K | 11 | |
| 15 |
| Thermal Expansion, µm/m-K | 13 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.5 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.6 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 12 |
| Density, g/cm3 | 8.2 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 120 | |
| 39 |
| Embodied Water, L/kg | 290 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 360 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 | |
| 390 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 26 |
| Strength to Weight: Axial, points | 26 | |
| 36 |
| Strength to Weight: Bending, points | 22 | |
| 29 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 4.0 |
| Thermal Shock Resistance, points | 21 | |
| 22 |
Alloy Composition
| Aluminum (Al), % | 1.8 to 2.4 | |
| 0 |
| Carbon (C), % | 0.15 to 0.25 | |
| 0 to 0.15 |
| Chromium (Cr), % | 24 to 26 | |
| 15 to 18 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 8.0 to 11 | |
| 65.6 to 73.9 |
| Manganese (Mn), % | 0 to 0.15 | |
| 4.0 to 6.0 |
| Nickel (Ni), % | 59.2 to 65.9 | |
| 4.0 to 6.0 |
| Nitrogen (N), % | 0 | |
| 0.080 to 0.2 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 3.0 to 4.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.040 |
| Titanium (Ti), % | 0.1 to 0.2 | |
| 0 |
| Yttrium (Y), % | 0.050 to 0.12 | |
| 0 |
| Zinc (Zn), % | 0.010 to 0.1 | |
| 0 |