N06035 Nickel vs. C33200 Brass
N06035 nickel belongs to the nickel alloys classification, while C33200 brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is N06035 nickel and the bottom bar is C33200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 100 |
| Elongation at Break, % | 34 | |
| 7.0 to 60 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 84 | |
| 40 |
| Shear Strength, MPa | 440 | |
| 240 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 320 to 520 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 110 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 1030 | |
| 130 |
| Melting Completion (Liquidus), °C | 1440 | |
| 930 |
| Melting Onset (Solidus), °C | 1390 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 380 |
| Thermal Expansion, µm/m-K | 13 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 24 |
| Density, g/cm3 | 8.4 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 2.6 |
| Embodied Energy, MJ/kg | 140 | |
| 44 |
| Embodied Water, L/kg | 330 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 35 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
| 60 to 960 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 22 | |
| 11 to 17 |
| Strength to Weight: Bending, points | 20 | |
| 13 to 17 |
| Thermal Shock Resistance, points | 17 | |
| 11 to 17 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.4 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 32.3 to 34.3 | |
| 0 |
| Cobalt (Co), % | 0 to 1.0 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 65 to 68 |
| Iron (Fe), % | 0 to 2.0 | |
| 0 to 0.070 |
| Lead (Pb), % | 0 | |
| 1.5 to 2.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Molybdenum (Mo), % | 7.6 to 9.0 | |
| 0 |
| Nickel (Ni), % | 51.1 to 60.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tungsten (W), % | 0 to 0.6 | |
| 0 |
| Vanadium (V), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 29 to 33.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |