N06035 Nickel vs. S40977 Stainless Steel

N06035 nickel belongs to the nickel alloys classification, while S40977 stainless steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is N06035 nickel and the bottom bar is S40977 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 34
21
Fatigue Strength, MPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 84
76
Shear Strength, MPa 440
320
Tensile Strength: Ultimate (UTS), MPa 660
510
Tensile Strength: Yield (Proof), MPa 270
310

Thermal Properties

Latent Heat of Fusion, J/g 340
270
Maximum Temperature: Mechanical, °C 1030
720
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 450
480
Thermal Expansion, µm/m-K 13
10

Otherwise Unclassified Properties

Base Metal Price, % relative 60
6.5
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 10
1.9
Embodied Energy, MJ/kg 140
27
Embodied Water, L/kg 330
97

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
92
Resilience: Unit (Modulus of Resilience), kJ/m3 170
250
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
18
Strength to Weight: Bending, points 20
18
Thermal Shock Resistance, points 17
18

Alloy Composition

Aluminum (Al), % 0 to 0.4
0
Carbon (C), % 0 to 0.050
0 to 0.030
Chromium (Cr), % 32.3 to 34.3
10.5 to 12.5
Cobalt (Co), % 0 to 1.0
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 0 to 2.0
83.9 to 89.2
Manganese (Mn), % 0 to 0.5
0 to 1.5
Molybdenum (Mo), % 7.6 to 9.0
0
Nickel (Ni), % 51.1 to 60.2
0.3 to 1.0
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015
Tungsten (W), % 0 to 0.6
0
Vanadium (V), % 0 to 0.2
0